35 Search Results

Ultra-high-temperature ceramics (UHTCs), including TiC, Ti¹¹B₂, and Zr¹¹B₂, show great potential for plasma-facing components due to their excellent high-temperature properties prior to irradiation. However, their response to neutron irradiation remains insufficiently understood, limiting robust assessment of their viability for fusion energy applications. Here, this study examines the thermal conductivity, dimensional stability and microstructure of TiC, TiB₂, and ZrB₂ following neutron irradiation at temperatures of 200–1000 °C and fast neutron fluences of 2.0 × 10²⁵ to 1.1 × 10²⁶ n/m² (E > 0.1 MeV). Lattice swelling measured by synchrotron X-ray diffraction in all three UHTCs was maximized at 200 °C andmore » decreased with increasing irradiation temperature, with no evidence of amorphization observed at 200 °C. Above 600 °C, significant macroscopic volume swelling was observed in irradiated Ti¹¹B₂ and Zr¹¹B₂, but not in TiC, likely due to cavity formation in the diborides. The post-irradiation thermal conductivity, measured at the irradiation temperature, ranged from 28 to 45 W/m·K, representing a 34–45% reduction relative to the unirradiated material. Notably, neutron-irradiated UHTCs exhibit recoverable thermal conductivity at elevated temperatures, comparable to ferritic–martensitic steels and potentially superior to W when transmutation effects are considered, highlighting promise for shielding or armor plasma-facing components. At 600 °C, both thermal conductivity degradation and lattice swelling saturated at doses exceeding 2–4 dpa.« less

Predicting the mechanical performance of structural alloys from their evolving microstructure remains a major challenge in materials science, particularly for nuclear structural materials, where irradiation-induced defects span multiple types and length scales and interact through complex mechanisms. The dispersed barrier hardening (DBH) [1] and Friedel–Kroupa–Hirsch (FKH) [2,3] models have been widely used to evaluate the hardening contributions of individual obstacles and to estimate tensile strength from quantified microstructures; however, when multiple size-dependent obstacles coexist and evolve, predicting temperature-dependent tensile strength becomes significantly more complex, and a fully consistent hardening model is still lacking. Transmission electron microscopy (TEM) plays a centralmore » role in refining hardening models and enabling predictive assessments of tensile strength evolution by providing quantitative characterization of dislocations, irradiation-induced defects (e.g., dislocation loops and cavities), precipitates, and grain structure (Fig. 1.). These experimentally measured defect densities are incorporated into physically based hardening models with size- and shape- dependent obstacle strengths [4], using root-sum-square superposition for obstacles of comparable strength and linear superposition for dissimilar ones [5]. In addition, recent advances in TEM [6-8], including high-resolution imaging, 4D-STEM strain mapping, EDS/EELS elemental analysis, and flash-polishing-based TEM specimen preparation and extraction-replica methods (Fig. 2), further improve the accuracy of microstructural quantification. By comparison with prior studies as well as our own results, we show that when TEM-derived microstructural information is carefully integrated with physically grounded hardening models, yield strength (or irradiation-induced hardening) measured at room temperature can be predicted with good quantitative agreement across multiple alloy classes. In-situ TEM combined with high-temperature mechanical testing represents an important next step for refining hardening models by directly probing dislocation–obstacle interactions across varying irradiation doses and temperatures [9]. Because the barrier strength factor (α) depends on both temperature and obstacle size, it should not be treated as a constant fitting parameter; rather, it must be explicitly evaluated to achieve physically meaningful predictions of mechanical behaviour at operating temperatures. This presentation therefore discusses why all strengthening contributions (e.g., Peierls stress, solid-solution strengthening, voids, bubbles, dislocation loops, dislocation lines, and grain boundaries) must be considered collectively, why appropriate superposition methods are essential when obstacles possess different barrier strength factors, how hardness measurements can be meaningfully related to tensile properties, and how TEM-derived microstructural information can be systematically incorporated into hardening models. More broadly, it outlines a pathway toward microstructure-informed prediction of mechanical properties and supports the goal of establishing science-based tools for evaluating structural materials in extreme environments [10].« less

Here, this study investigates the microstructural evolution of pure tungsten irradiated under thermal-neutron shielded and mixed spectrum conditions in the High Flux Isotope Reactor (HFIR). Four samples were irradiated at temperatures from 570 °C to 1130 °C up to 0.73 dpa. Neutron spectrum significantly influenced the accumulation of transmutation products, with Re+Os content estimated at ∼0.3–0.6% under thermal-neutron shielded conditions and ∼5.2% under the mixed spectrum condition. Irradiation temperature strongly influences tungsten’s microstructure, with dislocation loops and fine voids forming at lower temperatures and only larger voids and Re/Os segregation observed at higher temperature. Under thermal-neutron shielded conditions, dislocation loopsmore » and voids were observed at 570 °C and 790 °C. At the highest irradiation temperature (1130 °C), dislocation loops were no longer observed, while larger but less dense voids remained. Re and Os segregation to void surfaces was evident at 790 °C and 1130 °C, though no precipitation was observed. In contrast, under the mixed-spectrum condition, both spherical and needle-like Re/Os-rich precipitates were observed, frequently accompanied by large voids. Dislocation loops were not observed, but loop-like contrast within the precipitates suggests they may have nucleated on pre-existing loops. Irradiation-induced hardening was assessed for the shielded samples at 570 °C and 790 °C. Dispersed barrier hardening (DBH) analysis, based on TEM-resolved defects, revealed that voids were the dominant contributors to hardening, consistent with literature results. A schematic model is proposed to describe defect and precipitate evolution in tungsten under fusion-relevant transmutation-to-dpa conditions.« less

Focused ion beam (FIB) milling has become the dominant approach for site-specific transmission electron microscopy (TEM) specimen preparation; however, FIB damage remains a critical limitation for reliable microstructural characterisation, particularly in radiation effects studies. Tungsten is especially susceptible to FIB damage due to its high nuclear stopping power, which promotes the formation and strong diffraction contrast of FIB-induced ‘black spot’ defects that are indistinguishable from very fine irradiation-induced loops/defects resulting from low to intermediate temperature neutron irradiation. In this work, flash electropolishing is systematically evaluated as a post-FIB treatment for minimising preparation-induced artefacts for TEM analysis of tungsten-based alloys. Usingmore » a range of non-, ion-, and neutron-irradiated tungsten materials, the effectiveness of flash electropolishing has been assessed through direct comparison with conventional FIB and plasma-FIB preparation including low-energy Ga, Ar, Xe ion cleaning. The results demonstrate that flash electropolishing effectively removes FIB-damaged layers and ‘black spot’ defects, thereby enabling reliable observation of irradiation-induced dislocation structures. Key processing parameters governing flash electropolishing quality – including lamella thickness, applied voltage, polishing duration, electrolyte chemistry, and cathode geometry – have been systematically evaluated, and clear criteria were established for determining when flash electropolishing is required to ensure reliable microstructural analysis. This work also provides practical guidance for implementing flash electropolishing as an artefact-controlled specimen-preparation approach for TEM characterisation of FIB-produced specimens. The systematic protocol can be extended to other, non-tungsten materials.« less

Functional hydrides are promising candidates for advanced nuclear reactors, particularly in portable or transportable applications, due to their high hydrogen-retention capabilities, enabling efficient neutron moderation, and compact reactor design. However, hydrogen mobility in hydrides at elevated irradiation temperatures poses significant technological challenges, necessitating a comprehensive understanding of their irradiation behavior. Furthermore, this study investigated the microstructural and chemical stability of neutron-irradiated yttrium hydrides to assess their hydrogen-retention capacity. A targeted literature review was also conducted to contextualize neutron-irradiation effects on functional hydrides with regards to structural stability and hydrogen retention. Experimental characterizations revealed that, at high temperatures, irradiated hydrides retainedmore » their phase stability, which was likely enhanced by irradiation-induced microstructure evolution. Notably, an amorphous yttrium and oxygen -rich surface layer was present at the free surface of the hydride. Its thickness decreased while a continuous crystalline Y-O-rich layer was formed with increasing neutron damage. Additionally, the number density of dislocation loops and cavities generally increased as a function of neutron dose. First-principles calculations of hydrogen behavior within yttrium vacancy clusters in yttrium hydrides demonstrated vacancy-size-dependent hydrogen stability and configuration, highlighting the role of vacancy geometry in regulating hydrogen retention. Thus, the presence of irradiation-induced dislocation loops and cavities were hypothesized to improve hydrogen retention. Collectively, these findings advance the understanding of hydride behavior under neutron irradiation as well as their technological readiness for portable or transportable nuclear reactors.« less

PdO/γ-Al₂O₃ catalysts are one of the most active catalytic components for the complete oxidation of methane. Under reaction conditions, especially in a wet feed, the catalysts suffer severe performance degradation. This study establishes a series of testing protocols to systematically investigate the causes of catalyst deactivation under methane oxidation reaction conditions. Four distinct catalyst deactivation modes are identified. Two of the deactivation modes are directly related to H₂O, either from the feed gas or as a part of the reaction products, with one (Mode 2) being attributed to the formation of surface hydroxyl groups and the other (Mode 3) tomore » the competitive adsorption of H₂O on the catalysts. The impact of the two deactivation modes is acute and severe but reversible. In contrast, the other two deactivation modes are gradual and persistent but irreversible. Both modes are induced by CH₄ oxidation reaction, with the impact of a wet feed (Mode 4) being substantially more severe than that of a dry feed (Mode 1). The major cause of the irreversible catalyst deactivation is attributed to surface reconstruction of PdO nanoparticles, which behaves as a passivation layer lowering the number of coordinately unsaturated Pd sites for CH₄ activation. Although the passivation layer is relatively stable against thermal or hydrothermal treatment, it is not completely inert. Formation and partial regeneration of the passivation layer is a highly dynamic process and heavily depends on the reaction temperature: a lower reaction temperature (≤ 450 ℃) can lead to quicker catalyst deactivation; but a higher reaction temperature (between 500 – 550 ℃) can result in a greater extent of catalyst deactivation.« less

Glassy carbon, a monoatomic allotrope of carbon, is a candidate material for components in fission nuclear power systems due to its radiation tolerance. This article presents comprehensive electron microscopy data revealing the effects of neutron and electron irradiation on glassy carbon. For comparison, additional data are provided for pyrolytic graphite and carbon fibers, materials that exhibit similar structural behavior under irradiation. In situ electron irradiation experiments further illustrate the real-time microstructural evolution of glassy carbon during exposure. The dataset is organized into five parts: (1) transmission electron microscopy (TEM) micrographs of as-received and neutron-irradiated glassy carbon; (2) TEM micrographs ofmore » neutron-irradiated graphite; (3) TEM micrographs of unirradiated and irradiated carbon–carbon composites; (4) TEM micrographs of pyrolytic carbon specimens in both conditions; (5) scanning transmission electron microscopy (STEM) micrographs of as-received and neutron-irradiated glassy carbon and (6) in situ electron irradiation data of a glassy carbon particle. These datasets provide valuable insights into radiation-induced structural changes in carbon-based materials relevant to nuclear applications.« less

Ultra-high temperature ceramics (UHTCs) offer several potential advantages as plasma-facing components (PFCs) in fusion reactors due to their extreme melting points, tailorable thermal conductivity, and attractive unirradiated mechanical properties including fracture toughness comparable or superior to tungsten. Here, recent developments and material properties of UHTCs are briefly reviewed, along with an overview of limited studies on their responses to neutron irradiation and an evaluation of plasma-surface interactions. Five key research pathways, primarily focused on irradiation effects, for advancing UHTCs in PFC applications are discussed: (1) assessing irradiation effects on the coupled thermal–mechanical performance (2) addressing the lack of studies onmore » irradiation, plasma-surface interactions, and their synergistic effects; (3) investigating high-temperature (>1000 °C) neutron irradiation effects critical for PFC performance; (4) optimizing multi-component UHTC compositions or composites to improve thermal or mechanical properties; (5) enhancing radiation resistance to mitigate microcracking and void swelling through strategies such as increasing sink strength by reducing grain size, introducing fine particles, and leveraging complex concentrated alloy concepts.« less

This study investigated the crucial aspects of thermal and irradiation stability in precipitation hardened Haynes 282 Ni-based superalloy. The Haynes 282 Ni-based alloy was irradiated by 8 MeV Ni³⁺ ions to assess its resistance to phase instabilities and mechanical property alterations. The mid-range doses (at a depth of ∼1 µm) were 1 and 10 displacements per atom (dpa) at temperatures of 600°C and 750°C. Nanoindentation tests provided insights into bulk equivalent hardness of the irradiated and pristine regions, while scanning transmission electron microscopy (STEM) and energy dispersive X-ray spectroscopy (EDS) were used to examine the microstructural evolution of irradiation-induced defectsmore » and γ′ -Ni₃ (Al, Ti) precipitates and defect structure under irradiation. These precipitates, with an average diameter of 29 nm and a number density of 5 x 10²¹ /m³, acted as robust dispersion strengthening agents with high radiation point defect sink strength. Remarkably, irradiation did not significantly alter the size or number density of the γ′ precipitates, indicating exceptional thermal stability and radiation resistance of these precipitates at the examined conditions. Radiation-induced dislocation loops were observed at 600°C, albeit without a substantial impact on mechanical properties due to the dominance of γ′ precipitates on the overall alloy strength. The superior stability of γ′ precipitates observed in this study contrasts with several previous research findings on Ni-based alloys that reported poor precipitate stability. Plausible reasons for this difference are discussed. Moreover, this work explicitly outlines a physically grounded approach to ensure accurate microstructure-hardness correlations and clarifies the hardening model by addressing common misapplications of superposition in prior studies.« less

This research aims to explore an accelerated development path for oxide dispersion-strengthened (ODS) alloys by integrating additive manufacturing (AM) technologies with recent advances in ODS materials and traditional manufacturing methods. Novel AM and post-build processing routes have been developed for ODS austenitic alloys, specifically Fe-Cr-Ni alloys like 316L and 316H. Electron microscopy and mechanical characterizations were conducted to evaluate the effects of process variables on microstructure and properties, aiming for an economically feasible route property optimization. Traditionally, ODS alloy production involves multi-day high-energy mechanical milling of alloy powder with yttria (Y₂O₃) followed by powder consolidation via extrusion or other methodsmore » and additional thermomechanical processing (TMP) for property control. Here, to address these challenges associated with this complex and costly approach, we propose exploring alternative, cost-effective processing routes focusing on AM and traditional TMP methods. The new ODS alloy processing routes have achieved up to a 400% increase in yield strength and a 60% increase in ultimate tensile strength compared to wrought stainless steels while still maintaining significant ductility and fracture toughness. This paper details the novel and economical AM-based processing routes for ODS austenitic alloys, combined with post-build TMPs, and discusses the mechanical and microstructural characteristics of the developed materials.« less